| model | WL85 |
| color | White |
| Density (g/cm3 @ 25 ℃) | 1.11-~1.15（1.12~1.18） |
| Curing depth (mm) | 0.14~0.16 |
| Critical Exposure (mJ/cm2) | 7.1~8.1 |
| Construction layer thickness (mm) | 0.05~0.12 |
| Hardness (D) | 78~90 |
| Flexural modulus (MPa) | 2,675-2,765 |
| Bending strength (MPa) | 70- 76 |
| Tensile modulus (MPa) | 2,621-2,775 |
| Tensile strength (MPa) | 44-56 |
| elongation at break | 7 -12% |
| Notched impact strength (J/m) | 29 - 39 |
| Heat distortion temperature (°C) | 70~85 |
| Glass transition temperature (°C) | 80~95 |